Engineering :: Building Materials
|
|
|
|
|
121. |
A good Portland cement when tested for fineness, the percentage of residue left after sieving in 90 micron IS sieve should not exceed 10 percent. |
Answer: Option A
Explanation:
|
122. |
Le-chatelier method is used to determine |
A. |
initial setting of cement |
B. |
fineness of cement |
C. |
soundness of cement |
D. |
normal consistency of cement |
Answer: Option C
Explanation:
|
123. |
The expansion of cement should not exceed |
Answer: Option B
Explanation:
|
124. |
The normal consistency of Portland cement is about |
Answer: Option D
Explanation:
|
125. |
The initial setting time of rapid hardening cement should not be less than |
A. |
30 min |
B. |
1 hour |
C. |
4 hours |
D. |
8 hours |
Answer: Option A
Explanation:
|
126. |
The final setting time of ordinary cement should not be more than |
A. |
2 hours |
B. |
4 hours |
C. |
8 hours |
D. |
10 hours |
Answer: Option D
Explanation:
|
127. |
The addition of pozzolana to Portland cement causes |
A. |
less heat of hydration |
B. |
increase in shrinkage |
C. |
decrease in permeability |
D. |
all of these |
Answer: Option D
Explanation:
|
128. |
The rate of hydration and hydrolysis of cement depends upon its |
A. |
soundness |
B. |
fineness |
C. |
setting time |
D. |
tensile strength |
Answer: Option B
Explanation:
|
129. |
The compressive strength of ordinary cement is less than its tensile strength. |
Answer: Option B
Explanation:
|
130. |
The percentage of the residue left after sieving good Portland cement in 90 micron sieve should not exceed |
Answer: Option B