Engineering :: Building Materials
|
|
|
|
|
111. |
The ultimate strength of cement is provided by |
A. |
silica |
B. |
di-calcium silicate |
C. |
tri-calcium silicate |
D. |
tri-calcium aluminate |
Answer: Option B
Explanation:
|
112. |
A good quality cement should have higher percentage of |
A. |
silica |
B. |
free lime |
C. |
di-calcium silicate |
D. |
tri-calcium silicate |
Answer: Option D
Explanation:
|
113. |
The strength of white cement is |
A. |
equal to |
B. |
less than |
C. |
greater than |
Answer: Option B
Explanation:
|
114. |
The percentage of the slag component of Portland-slag cement varies from |
A. |
10 to 40% |
B. |
40 to 70% |
C. |
70 to 80% |
D. |
80 to 90% |
Answer: Option B
Explanation:
|
115. |
The rapid hardening Portland cement has a |
A. |
lower heat of hydration |
B. |
higher heat of hydration |
C. |
lower shrinkage coefficient |
Answer: Option B
Explanation:
|
116. |
The initial setting of cement is caused due to |
A. |
di-calcium silicate |
B. |
tri-calcium silicate |
C. |
tri-calcium aluminate |
D. |
tri-calcium alumino ferrite |
Answer: Option C
Explanation:
|
117. |
The hapd hardening Portland cement is obtained by |
A. |
grinding the clinker to a high degree of fineness |
B. |
adding calcium sulphate to the mixture |
C. |
adding gypsum after grinding |
D. |
burning the mixture at a lower temperature |
Answer: Option A
Explanation:
|
118. |
The fineness of cement is tested by |
A. |
air-permeability method |
B. |
Le-chatelier method |
C. |
Vicat's apparatus |
D. |
all of these |
Answer: Option A
Explanation:
|
119. |
The soundness of cement is tested by |
A. |
air permeability method |
B. |
Le-chatelier method |
C. |
Vicat's apparatus |
D. |
all of these |
Answer: Option B
Explanation:
|
120. |
Vicat's apparatus is used to determine the |
A. |
initial setting time of cement |
B. |
final setting time of cement |
C. |
normal consistency of cement |
D. |
all of these |
Answer: Option D
Explanation:
|
Read more:
|
|