71. |
Low heat cement contains more lime than ordinary Portland cement. |
Answer: Option B
Explanation:
|
72. |
Blast furnace slag cement |
A. |
develops low heat of hydration |
B. |
has less early strength |
C. |
develops high heat of hydration |
D. |
has high early strength |
E. |
Both (a) and (b) |
|
|
Answer: Option E
Explanation:
|
73. |
Which of the following cements is expected to have the highest compressive strength after 3 days. |
A. |
ordinary Portland cement |
B. |
rapid hardening cement |
C. |
high alumina cement |
D. |
sulphate resisting cement |
Answer: Option C
Explanation:
|
74. |
For a structure subjected to the action of sea water, the cement used is |
A. |
rapid hardening cement |
B. |
low heat cement |
C. |
high alumina cement |
D. |
sulphate resisting cement |
Answer: Option C
Explanation:
|
75. |
The strength of concrete using air entraining cement gets reduced by |
A. |
5 to 10% |
B. |
10 to 15% |
C. |
15 to 20% |
D. |
20 to 25% |
Answer: Option B
Explanation:
|
76. |
"Colocrete" is the commercial term for |
A. |
high alumina cement |
B. |
coloured cement |
C. |
low heat cement |
D. |
rapid hardening cement |
Answer: Option B
Explanation:
|
77. |
Pezzolana is essentially a silicious material containing clay upto |
Answer: Option D
Explanation:
|
78. |
In the manufacture of possolana cement, the amount of pozzolana material added to ordinary Portland cement clinkers is about |
Answer: Option B
Explanation:
|
79. |
Which of the following statement is correct? |
A. |
Sulphate resisting cement is particularly used for canal lining. |
B. |
Low heat cement should not be used for thin concrete structures. |
C. |
Rapid hardening cement should not be used for massive concrete structures |
D. |
all of the above |
Answer: Option D
Explanation:
|
80. |
The degree of grinding of cement is called |
A. |
fineness |
B. |
soundness |
C. |
impact value |
D. |
bulking |
Answer: Option A
Explanation:
|